Hiflex White


Cemix® Hiflex White tile adhesive is a premium grade highly flexible polymer engineered white cement based water resistant adhesive for interior or exterior fixing of a wide range of tiles on to a variety of substrates, white powder complies with c1tes1. Cemix® Hiflex White tile adhesive is a highly flexible, polymer modified, cement based adhesive used for most internal external wall and floor applications including bathrooms, toilets, laundries, kitchens, decks, verandahs and existing tiles. Suitable over concrete, cement renders, screeds, fibrous cement sheeting, plasterboard and cemix approved waterproofing membranes. In conjunction with Cemix® Self Leveller, it can be used for under tile heating applications. When using with translucent tiles, the colour of the adhesive should be taken into consideration.

Typical Application / Uses:

  • For interior or exterior fixing of a wide range of tiles on to a variety of substrates.
  • Used for most internal external wall and floor applications including bathrooms, toilets, laundries, kitchens, decks, verandahs and existing tiles


  • Highly flexible
  • Polymer engineered
  • Water resistant
  • Suitable over concrete, cement renders, screeds, fibrous cement sheeting, plasterboard and Cemix® approved waterproofing membranes


Substrate Preparation:

The substrate should be free of dust, grease, wax, oil, dirt, loose plaster, laitance, curing compounds, paint and all other friable materials and contaminants likely to prevent the adhesive bonding. New concrete should be left with a wood float finish and sufficiently aged for a minimum of 28 days. Shiny smooth surfaces on old concrete should be acid etched or scabbled. Cemix® cement screeds/floor levelers/renders must be allowed to cure for a minimum of 7 days.

All substrates should be structurally sound, securely fastened and properly supported to eliminate any movement which may cause cracking. Cemix® Hiflex White is suitable for tiling over timber floors, provided that a fibre cement sheet tile underlay is initially installed over the timber floor.

All substrates that are suitable for tiling should be primed using undiluted Cemix® Cemlastic. For further information, contact the Cemix® Technical support.

Perform the substrate test:

No water absorbed - Mechanically prepare substrate.

Moderate water absorbed -Clean with damp sponge and water.

All water absorbed - Broom on liberal amounts of water.

This simple test is performed after vacuuming or sweeping a number of test areas and applying a single drop of fresh drinking water from the end of your finger. This should be approximately 20mm wide when it first hits the floor – if it beads and remains whole then “No water is absorbed”. If it loses all gloss within 20 - 60 seconds then “Moderate water is absorbed”. If the gloss disappears instantly or within 20 seconds then the substrate has “All water absorbed”. Look for different surface appearance in your floor and test each to ensure your test is representative of the whole area. Perform test in both a cool shaded area and an exposed sunny area if tiling externally.

Movement / Control Joints:

Movement joints must be incorporated at the design stage and in accordance with AS3958.1-2007 as follows:

1. Over movement joints in the background

2. At a junction between different backgrounds materials

3. At internal vertical corners and fixtures interrupting the tile surface e.g. columns

4. Around the perimeter of the tiling area

5. At a maximum of 5m intervals in a grid pattern.

Note: Movement joints should go right through the tile adhesive bed to the background and be kept free from dirt and adhesive droppings. Movement joints must not be less than 6mm or greater than 10mm wide. All movement joints that are 6mm wide can be filled with flexible sealant.


  1. Add approx. 200 - 300ml of clean water to a bucket for every 1Kg of Cemix® Hiflex White tile adhesive.
  2. Sprinkle powder slowly into the water, mixing constantly until a thick creamy toothpaste consistency is achieved – with no lumps.
  3. Allow to stand for 5 minutes and re mix and then the adhesive is ready to use.
  4. Do not aerate the mix by stirring over vigorously or for too long. The mix should be stiff enough


All workmanship must be carried out in accordance with AS3958.1-2007.

Spread the adhesive evenly with a 6mm X 6mm notched trowel for tiles up to 150mm X 150mm and for larger tiles use a 10mm X 10mm notched trowel. Lay the tiles with a good pressure, twisting to ensure good contact with the adhesive. In more demanding exterior situations, tile on tile applications or if tiles with high ribs or lugs are being used, it is preferable to spread the backs of the tiles with a thin layer of adhesive in addition to the adhesive being trowelled substrate, before laying. When adhering to non-porous surfaces or tiles, please ensure that a minimum of 90% of adhesive contact is achieved to the back of the tiles. For wall tiling a minimum final bed thickness between 1 - 3mm is recommended, whilst for floor tiling a minimum final bed thickness between 3 - 10mm is recommended. Do not spread more than 1m2 of adhesive at any one time as skinning may occur affecting final adhesion. Press tiles onto the adhesive before it skins and ensure that the tiles are fully supported with the adhesive with no voids. Occasionally, in order to ensure that full coverage is being maintained, a tile should be removed, the adhesive coverage noted and the tile be re-laid accordingly. Once the tiles have been laid, they must not be trafficked upon or disturbed for a minimum of 24 hours at 20oC. Allow 48 hours if temperature will fall below 20oC or tiling over Cemix® approved waterproofing membranes, non-porous substrates or tile-on-tile applications.


Grouting may be undertaken after 24 hours but allow a further 24 hours before general use. Allow joint widths of 1.5 - 5mm for walls and 3 - 15mm for floors as per AS/NZ 3958.1-2007. Thoroughly clean the surface of the tiles to remove all residue prior to the grout drying.

Technical Data:

Appearance – White Powder

Application Temp – 5 – 30oC

Yield / Coverage – Varies according to size from approximately: Approx. 0.85m2 per kg bag using a 6mm notched trowel and 0.60m2 using a 10mm notched trowel.

Bulk Density – 1kg/litre

Adjustment time at 18oC: 60 minutes

Pot life at 18oC: 60 minutes

Classification: CITES1

The data shown above reflects typical results based on laboratory testing under controlled conditions. Reasonable variations may occur on site.


  • Not suitable for tiling directly over flexible substrates, such as timber, plywood, particleboard, MDF and Masonite unless minimum 6mm thick fibre cement underlay sheet is securely fastened over timber, particleboard etc. Please ensure that there are adequate falls incorporated to prevent water ponding.
  • Not suitable for continuous water immersion applications, e.g. swimming pools and spas etc.
  • Not suitable for tiling over waterproofing membranes unless it is Cemix® approved.
  • Not suitable for tiling directly on to impervious non-absorbent surfaces like metals and plastics.
  • Not suitable for moisture sensitive tiles stones or green marble as warpage may occur. Brush apply the moisture sensitive stone with Cemix® Pavseal and then fix the sealed stone as normal after 4 - 5 hours – to avoid discolouration and moisture penetration.
  • Only to be used between 5oC - 30oC and avoid extreme windy locations.
  • External tiling must not to exceed 2.7m in height
  • Suspended concrete slabs must conform to AS/NZ3958.1-2007 for maximum deflection. Any post-tensioned concrete slab must be treated as a flexible substrate.


Twelve (12) months - unopened bags in dry weatherproof storage.


Remove excess adhesive from between the tiles and clean the tile faces with a damp sponge before the adhesive sets. Clean tools with water before the adhesive dries.


Being cement based, may cause respiratory, skin and eye irritation. Wet cement can be irritating and corrosive to eyes and skin; and may cause skin sensitization (dermatitis). Repeated inhalation may cause bronchitis, silicosis and lung cancer and increase risk of scleroderma.